Nnyocha nke ihe isi ike n'ichepụta ihe nchara isi awọ

---

Iji dozie nsogbu machining nke nkedo isi awọ n'ime ụlọ ọrụ, a na-enyocha ihe ndị mejupụtara na ihe onwunwe nke ezi ezi na ihe nkedo site na microscope anya, microscope eletrọn na-enyocha, Brinell hardness, micro Vickers hardness and spectrum analysis. Nsonaazụ na-egosi na ọdịnaya nke S na P nke 26 # pig iron dị n'elu akụkụ dị elu, ọdịnaya nke Si nke 22 # pig iron dị ala, ya mere ihe mejupụtara kemịkalụ adịghị eju njirisi. Ihe nkedo carbon nke ihe nkedo bụ 4.36%, nke bụ nke nkedo nha carbon dị elu. Oke Si na C bụ 0.46, nke dị n'akụkụ ala. Ọdịnaya nke Si na Mn na nkedo dị ala, na mgbakwunye na ọdịnaya nke Cr dị elu, nke zuru oke iji mepụta ihe na-ekpo ọkụ, enwere V element na nkedo karịa. microstructure nke nkedo bụ ferrite, pearlite, graphite na carbide. Akụkụ ụfọdụ nke carbide nwere Cr, V na ihe ndị ọzọ na-eme ka micro-alloying, na micro hardness karịrị 1 100 HV, nke bụ isi ihe na-akpata machining siri ike. Ya mere, iji meziwanye machining c apacity, nke mbụ, ọdịnaya nke V na Cr ekwesịghị gafere ọkọlọtọ. Nke abụọ, ọdịnaya nke Si kwesịrị ịba ụba ma buru ụzọ họrọ ịgbakwunye na inoculation. Maka ihe nkedo na-achọsi ike, enwere ike imebi carbide site na iji eserese eserese.

Nkuku ọcha nke ihe nkedo ígwè isi awọ nwere obere mgbidi bụ ntụpọ a na-ahụkarị na nkedo [1-4]. N'ozuzu, obere ihe nkedo nwere mgbidi dị gịrịgịrị ma na-atụba ya na ájá akwụkwọ ndụ akwụkwọ ndụ. Ọ bụ ezie na ihe mejupụtara kemịkalụ nke ígwè a wụrụ awụ ruru eru, n'ihi mmetụta nke ọkpụrụkpụ mgbidi nkedo na okpomọkụ nke ihe nkedo ahụ, akụkụ ndị dị arọ ma dị mkpa nke otu nkedo ahụ. Ma n'ime ma n'èzí nwere ike ịnweta nhazi dị iche. Karịsịa nkuku nke ihe nkedo na-adịkarị mfe ọnụ na-acha ọcha, nke na-akpata ihe isi ike na nhazi, na-akpata ihe a na-akpọ "ihe siri ike". Ọtụtụ akụkụ nke ihe nkedo isi awọ "ihe siri ike" na-eme n'akụkụ akụkụ ahụ siri ike. Dị ka: ọnụ na nkuku, grooves, convex na-ebupụta, na-ebupụta, wdg. Ihe ike ike nwere ọtụtụ ihe na-eme na ọchịchọ nke ọcha ọnụ. N'ịchọ na nsogbu machining siri ike na mmepụta nke nkedo nke ụlọ ọrụ ụfọdụ, akwụkwọ a na-eduzi ọmụmụ ihe nhazi, nyochaa ihe ndị na-akpata "ihe siri ike", na-atụ aro ngwọta kwekọrọ.

1 Ngwa na ụzọ nnwale

A na-enyocha ígwè ezi 22 #, 26 # na igwe nkedo nọmba 0 # na saịtị. A na-eme nlele site na ịcha waya n'otu n'otu, na nyocha nke anụ ahụ anya na nyocha anụ ahụ. Chemical na nkedo ígwè na nkedo
Nnwale ihe mejupụtara iji wepu mmetụta nke ihe nchọta na arụmọrụ nhazi nke nkedo. Emere ihe nkedo ahụ maka nleba anya n'ọkpụkpụ igwe na ZEISS anya na nyocha microscopes, HBS-3000 dijitalụ Brinell hardness tester na HTM-1000TM micro hardness tester ka ejiri mee nnwale ike. Egosiri ihe mejupụtara kemịkalụ nke igwe ezi na ihe nkedo na tebụl 1.

C	Si	Mn	P	S	W	Te	Bi	Cr	V	Ce	B	Mo
0 # 3.73	1.75	0.17	0.15	0.12	≤0.01		5		5	0.11	0.027	0.01	0.004	4	≤0.01
22 # 4.08	1.86	0.055	0.07	0.02	≤0.01		5		5	≤0.010	≤0.010	0.01	0.002	2	≤0.01
26 # 3.38	2.51	0.17	0.45	0.095	≤0.01		5		5	0.023	0.044	0.01	0.008	9	≤0.01

2.1 Nyocha ihe mejupụtara kemịkalụ

Mgbe carbon nkedo isi awọ dị n'ụdị carbides, ọ na-abawanye ọchịchọ nke ịcha ọcha, nke na-eme ka igwe na-arụ ọrụ siri ike ma na-ebute nsogbu a na-akpọ "ihe siri ike". Ya mere, ígwè nkedo isi awọ kwesịrị ibelata ọchịchọ nke ịcha ọcha, nke mere na carbon dị n'ụdị graphite. Ihe dị iche iche nwere mmetụta dị iche iche na usoro graphitization, na ụfọdụ nkume na-agba ọsọ
Inking, ụfọdụ na-ebelata graphitization. N'ikwu okwu n'ozuzu, ọtụtụ n'ime ihe ndị nwere ike ime ka ike dị n'etiti ígwè na carbon carbon na-eme ka ike gbasaa onwe ya nke atom ígwè nwere ike ịkwalite graphitization nke ígwè nkedo; ma ọ bụghị ya, ọ ga-egbochi graphitization nke nkedo ígwè, ya bụ, na-amụba ọchịchọ nke ọnụ ọcha. . Maka ịnwale igwe nkedo
Ogo nke ígwè ezì na mkpochapụ mmetụta nke ihe ndị na-emepụta ihe na-acha ọcha nke nkedo. A nwalere ihe ise na ihe na-acha ọcha nke akụrụngwa na nkedo. A nwalere nlele ọ bụla maka ihe iri na atọ. Ngụkọta nke 13 nke ígwè ezi na nkedo ka nwalere. E gosipụtara ihe mejupụtara kemịkalụ na tebụl 39.

Ọkọlọtọ nke igwe ezì nke China (GB/T 718-2005) [5], na ọkọlọtọ, ọdịnaya Si nke 22 # pig iron bụ 2.00% ~ 2.40%, yana ọdịnaya Si nke 26 # pig iron bụ 2.40% ~ 2.80%. Dị ka Tebụl 2 si kwuo, ígwè ezi nke ụlọ ọrụ 22 # na 26 # gosiri na ọdịnaya Si nke 22 # pig iron bụ 1.86, nke na-emezughị oke ala nke ọkọlọtọ.
Ọ ruru ọkọlọtọ, yana ọdịnaya Mn dịkwa ala. 26# pig iron P na S dị elu nke ukwuu, ọdịnaya P ruru ọkwa 5, ọdịnaya S karịrị ọkọlọtọ, ma nwee ụfọdụ Cr. Ngwakọta nnwale nke nkedo 0 # na-egosi na ọ bụ naanị ọdịnaya Cr nke ihe ndị na-acha ọcha erutela nchacha ọcha, na ọdịnaya nke ihe ndị ọzọ achọpụtara erubeghị ọdịnaya kacha nta nke na-eme ka ịcha ọcha, ya mere mmetụta ahụ adịghị elele. E jiri ya tụnyere nhọrọ nke ihe ise dị na "Casting Handbook" [6], a pụrụ ịhụ na carbon ọdịnaya nke nkedo n'ime ọmụmụ ihe a dị oke elu, ọdịnaya Si dị ntakịrị, na ọdịnaya Mn dị ntakịrị. .

2.2 Nnwale ike ike

Na HBS-3000 dijitalụ ngosi Brinell hardness tester, ule bụ 1875 N, indenter dayameta bụ 2.5 mm, na ike nke 5 ule na-egosi na Tebụl 2. Na dijitalụ microhardness tester, na-acha ọcha ebe na anya foto. eji microhardness akara. E gosipụtara nsonaazụ ya na Tebụl 3. Ya mere, ọ bụ ezie na nkezi macroscopic hardness nke matrix dị nnọọ ala, naanị Brinell hardness bụ banyere 145 HB, ike nke mpaghara mpaghara ya dị elu, na-erute Vickers hardness nke banyere 1 000 HV. . Obere olulu, otú ahụ ka ike siri ike dị elu. Dị ka akwụkwọ akụkọ si kwuo, ike nke phosphorus eutectic bụ 500 ~ 700 HV, ledeburite ≤ 800 HV, na carbide> 900 HV.

Ya mere, nsonaazụ nyocha nke siri ike na-egosi na ebe a na-acha ọcha na-esi ike na cementite carbide siri ike, nke bụ isi na-ewepu eutectic phosphorus, nke bụ isi ihe kpatara ihe siri ike. Iji chọpụta n'ụzọ ziri ezi ihe mejupụtara nke carbide a, a chọrọ nyocha ụdị ume ike.

2.3 Nyocha ụdị ike ike

A na-egosi mmụba akụkụ nke mpaghara ọcha anya na Fig. 2 na Fig. 3. A na-ejikọta ya site na nkesa nke oghere ndị a na-agbanye na matriks na njirimara eutectic. Ya mere, nyocha nke ike nke mpaghara a na-egosi na ihe ndị dị n'ime ebe a na-ewepụ ihe bụ Fe, P na C element, ya mere a na-ekpe ya ikpe dị ka Fe3 (C, P), P element na-echekwa.
Nkewa. The P element na recessed akụkụ dị elu, ọ bụghị a eutectic ngwaahịa, ma oghere kpụrụ site ikpeazụ solidification na shrinkage. Ọgụgụ 4 Nsonaazụ nyocha nke ike ike na-egosi na mgbakwunye na ihe Fe, P na C, mpaghara ọcha nwere Cr na V, na-akpụ carbide alloy, nke siri ike ma sie ike.
Were ịkpụ.

2.4 Nyocha nhazi

Foto anya na-egosi nhazi metallographic nke ihe nkedo mere site na etching na 4% nitric acid mmanya, dị ka e gosiri na foto 5. N'ime ha, a, b, c, na d bụ ​​isi nhazi nke nkedo, na e, f. g, na h bụ akụkụ akụkụ nke nkedo ahụ. a, b, c, d na e, f, g, h kwekọrọ na foto anụ ahụ ugboro 50, 100, 200 na 1,000. E gosipụtara foto anụ ahụ a na-enyocha na eserese 6, na akụ ahụ na-atụ aka na mpaghara ọcha na foto anụ ahụ kwekọrọ, nke bụ carbide. Ebe mgbochi ọcha bụ carbide, flakes bụ graphite, ebe isi awọ bụ pearlite. Enwere ike ịhụ na ihe owuwu metallographic bụ ferrite + pearlite + graphite + carbide, nke nwere oghere. O doro anya na ịdị ọcha nke akụkụ dị njọ karịa nke obi. N'iji ya tụnyere GB/T7216-2009, enwere ike ịhụ na [7], anụ ahụ obi bụ nke mbụ.
Ụdị graphite F nke raw kpakpando nwere ogologo ihe dịka 150 μm na obosara nke ihe dịka 5 μm. Nke a bụ ígwè a wụrụ awụ nke nwere nnukwu carbon n'okpuru ọnọdụ jụrụ oyi dịtụ ukwuu. Nhazi oyi akwa dị mma graphite gbakọtara na nkesa chrysanthemum nke ụdị B graphite. Ogologo ya dị ihe dịka 100 μm na obosara bụ 3 μm. Kpebie ọnụ ọgụgụ nke carbides
Ọnụ ọgụgụ nke carbide dị n'ime anụ ahụ obi bụ ihe dịka 5%, na-eru ọkwa 3. Ọnụ ọgụgụ nke carbides na nsọtụ anụ ahụ bụ ihe dịka 10%, na-eru ọkwa 4. Mgbe carbon dị n'ụdị graphite, a pụrụ iji graphite mee ihe maka ya. mmanu mmanu n'oge machining, na ịcha dị mfe. Mgbe carbon dị n'ụdị carbide (Fe3C), n'ihi na Fe3C cementite siri ike na kenkuwa, machining siri ike, karịsịa ma ọ bụrụ na o nwere ihe ndị ọzọ alloying (dị ka Cr), alloy cementite ((Fe, M) 3C) Ngwakọta a bụ. siri ike na nke siri ike ịkpụ, na nsogbu nke a na-akpọ "ihe siri ike" na-apụta mgbe a na-arụ ọrụ [8]. Ya mere, na usoro nkedo nke akụkụ isi awọ isi awọ, ọ dị mkpa iji belata ọnụ ọgụgụ nke carbon iji zere ọdịdị nke carbides, ma mee ihe ụfọdụ iji kwalite carbon graphitization ma ọ bụrụ na ọ dị mkpa.

3 Nyocha na mkparịta ụka

Ihe ndị bụ isi na-emetụta ọrụ nhazi nke nkedo bụ ihe mejupụtara kemịkalụ nke ihe nkedo na ọnụego jụrụ oyi siri ike. Ọdịnaya carbon na ọdịnaya silicon dị na kemịkalụ nke igwe nkedo bụ ihe abụọ kacha mkpa na-achịkwa. Ọnụọgụgụ jụrụ oyi nke nkedo na-adabere na ọkpụrụkpụ mgbidi nke nkedo ahụ. Mgbe ọdịnaya nke carbon na silicon na nkedo ígwè na-adịgide adịgide, ka mgbidi nkedo ahụ na-adịwanye njọ, otú ahụ ka ọdịdị nke nkedo na-esiwanye ike. Mgbe ọkpụrụkpụ mgbidi nke nkedo na-adịgide adịgide, ka ọnụọgụ carbon na silicon dị na nkedo nkedo na-abawanye, otú ahụ ka ogo nke eserese nke nkedo na-adịwanye nke ọma.

Ihe nkedo carbon nke ihe nkedo n'ọmụmụ ihe a bụ 4.36%, nke bụ ihe nkedo dị elu nke carbon; Si / C ruru 0.46, nke dị ala. Ịbawanye nha carbon na-eme ka flakes graphite dịkwuo oke, ọnụọgụ na-abawanye, ike na ike na-ebelata. Ịbawanye Si/C nwere ike ibelata ọchịchọ nke ọnụ ọcha.

Na mmepụta nke ígwè nkedo isi awọ, mmetụta nke ikpo oke ọkụ na mmetụta nke ime ime dịkwa mkpa ka a tụleghachi ya. Ịbawanye okpomọkụ nke ígwè a wụrụ awụ n'ime ebe ụfọdụ nwere ike ime ka nchacha graphite, nhazi matrix dị mma, ike nkwụsị na-abawanye, na ike na-ebelata. Ọ dị mkpa iji nlezianya tụlee ihe mejupụtara nke ụgwọ ahụ, akụrụngwa na-agbaze, na ihe ike nke mejupụtara kemịkalụ. Ọgwụgwọ inoculation bụ ịgbakwunye inoculant na ígwè a wụrụ awụ iji gbanwee ọnọdụ ọla nke ígwè a wụrụ awụ tupu ígwè ahụ a wụrụ awụ abanye n'ime oghere nkedo, na ịbawanye nucleus na-adịghị ahụ anya bụ nhazigharị graphite. Nke a na-emeziwanye microstructure na ịrụ ọrụ nke ígwè nkedo. Inoculants ndị a na-ahụkarị gụnyere ferrosilicon, silicon silicon na graphite. Ijikọta ngwaahịa anyị na ọnụ ahịa mmepụta anyị, a na-atụ aro ka iji ferrosilicon (75% silicon, ego mgbakwunye bụ ihe dịka 0.4% nke ịdị arọ nke ígwè a wụrụ awụ). Nke abụọ, barium ferrosilicon na strontium ferrosilicon. Ferrosilicon na-etinye mmetụta na-eme ngwa ngwa, na-eru elu n'ime 1.5 min, ma na-agbada na steeti na-adịghị ime mgbe 8 ~ 10 min, nke nwere ike ibelata ogo nke supercooling na anụ ọcha ọnụ, na-abawanye ọnụ ọgụgụ nke eutectic ụyọkọ, na-etolite A-ụdị. graphite, meziwanye ịdị n'otu nke ngalaba ahụ, ma mee ka mgbochi ahụ dịkwuo elu. Ike mgbagharị bụ 10-20MPa. Ọdịmma: adịghị mma iguzogide ire ere. Ọ bụrụ na ejighị usoro inoculation oge eme ihe, ọ dịghị mma maka nnukwu ọdịiche dị n'ụdị mgbidi na ogologo oge ịwụsa.

Barium ferrosilicon nwere ikike siri ike ịbawanye ọnụ ọgụgụ nke ụyọkọ eutectic ma melite otu ngalaba karịa ferrosilicon. Ikike iguzogide ọdịda siri ike, yana mmetụta inoculation nwere ike ịnọgide na-enwe maka nkeji 20. Kwesịrị ekwesị maka ọkwa dị iche iche nke akụkụ ihe nkedo isi awọ, karịsịa maka akụkụ buru ibu nke nwere mgbidi na ọnọdụ mmepụta na ogologo oge ịwụsa.

Strontium ferrosilicon nwere ikike mbelata ọcha dị elu 30% ruo 50% karịa ferrosilicon, ma nwee otu ngalaba ka mma yana ikike mgbochi ire ere karịa ferrosilicon. N'otu oge ahụ, ọ naghị amụba ọnụ ọgụgụ nke eutectic ụyọkọ, ọ dị mfe igbari, ma nwee obere slag. Akụkụ ndị nwere mgbidi dị obere, ọkachasị akụkụ chọrọ mbelata na ntapu nwere ụyọkọ eutectic dị elu achọghị.

Ọdịnaya Mn nke ihe nkedo na ọmụmụ a dị ala. Manganese n'onwe ya bụ ihe na-egbochi graphitization, ma manganese nwere ike ịkwụsị mmetụta siri ike nke sọlfọ na-acha ọcha. Ya mere, n'ime oke nke ịkwụsị mmetụta nke sọlfọ, manganese na-ekere òkè n'ịkwalite graphitization. Omume egosila na mmụba nke ọdịnaya manganese nwere ike ọ bụghị naanị ịbawanye ma mee ka pearlite dị ọcha, ma ọ dịghị emerụ ahụ iji mee ka nchịkwa nke sọlfọ dị mma. Ya mere, a na-atụ aro ka ịbawanye ọdịnaya Mn nke ọma.

Nkọwa 4

Isi ihe kpatara ihe siri ike nke igwe nkedo n'ime ọmụmụ ihe a bụ ọdịdị nke carbides cimentite, karịsịa carbides cementite nke alloys nwere Cr, V na ihe ndị ọzọ bụ isi ihe kpatara nsogbu igwe. Iji meziwanye nsogbu a, echiche mbụ bụ iji belata ma ọ bụ kpochapụ carbides na nzukọ ahụ. Ịgbanwe nhazi nke nkedo na imezi usoro mmepụta bụ ụzọ dị irè. Ejikọtara ya na ọnọdụ mmepụta ihe nkedo a kapịrị ọnụ, a na-atụnye aro mmepụta ndị a:

• (1) Iji mee ka ọdịnaya silicon dịkwuo elu, nhọrọ mbụ bụ ịgbakwunye inoculant tupu ịwụsa. Maka ferrosilicon (75% silicon), barium ferrosilicon na strontium ferrosilicon nwekwara ike iji dị ka oge wụsa na mmetụta na saịtị. A na-atụ aro iji inoculants compound (Si-Ba na RE-Si).
• (2) Mụbaa ọdịnaya manganese na nkedo iji mebie mmetụta ọnụ ọcha siri ike nke sọlfọ.
• (3) Meziwanye ogo ígwè ezi. 26#Pig iron P na S dị elu karịa.
• (4) Wedata ọdịnaya C na nkedo. Ọdịnaya dị elu nke Cr (> 0.1) na nkedo nwere ike mepụtalarị mmetụta nke ịcha ọcha. Cr nwere ike ịbawanye ike nke ukwuu ma mebie arụmọrụ igwe.

Njikọ na akụkọ a ： Nnyocha nke ihe isi ike n'ichepụta ihe nchara isi awọ

Nkwupụta Mbipụta: Ọ bụrụ na enweghị ntuziaka pụrụ iche, isiokwu niile dị na saịtị a bụ nke mbụ. Biko gosi isi mmalite maka ibipụta ya ọzọ: https: //www.cncmachiningptj.com/，thanks！

---

Lọ ahịa PTJ CNC na-arụpụta akụkụ nwere ezigbo ihe eji arụ ọrụ, izi ezi na nrụpụta site na igwe na plastik. 5 axis CNC egwe ọka dị.Igwe na-edozi alloy dị elu iche iche mkpu igwe ihe ndozi,Nkwanye monel,Igwe ihe omimi nke Geek,Carp 49 igwe,Ngwaọrụ Hastelloy,Ngwunye nitronic-60,Ndinam Hymu 80,Ngwá ọrụ ígwè machining, wdg. Ezigbo maka ngwa aerospace.CNC igwe na-arụpụta akụkụ ya na ezigbo ngwa ọrụ ya, izi ezi ya na ike ya site na igwe na plastik. 3-axis & 5-axis CNC milling available.We ga strategize na ị na-enye ndị kasị na-eri-irè ọrụ na-enyere gị aka iru gị lekwasịrị anya, Welcome to Kpọtụrụ anyị ( sales@pintejin.com ) ozugbo maka oru ohuru gi.